Test Items | Result | Inspection method |
Adhesion Strength (Base: Cement Mortar) w/o Primer | 17.3 kgf / cm2 | CNS 8083 |
Adhesion Strength (Base: Steel Board) w/o Primer | 13.8 kgf / cm2 | CNS 10757 |
Water Resistance (23℃,30 days) | Normal | CNS 10757 |
Water Permeability | 0.5 ML | CNS 4684 |
Tensile Strength | 37 kgf / cm2 | CNS 6483 |
Elongation Rate | 340 % | CNS 6483 |
Tear Resistance | 26 kgf / cm2 | CNS 6483 |
Compression Set Value( 70℃,22H ) | 105 % | CNS 6483 |
Coefficient of Elasticity | 8 % | CNS 6483 |
Viscosity(LV type, spindle No.3 , 3 rpm) | 25200 CP | CNS 5607 |
Solar Direct Reflectance(Test side: Gloss side)(300~2500nm) | 83.7 % | ISO 9050 |
ROHS ( Test ltems ) | Method(Refer to) | (Result)( No.1 ) | ( MDL ) |
Cadmium(Cd) | (1) | n.d. | 2 |
Lead( Pb ) | (2) | n.d. | 2 |
Mercury(Hg) | (3) | n.d. | 2 |
Hexavalent Chromium Cr(VI)by alkaline extraction | (4) | n.d. | 2 |
Sum of PBBs | (5) | n.d. | - |
Monobromobipheny1 | n.d. | 5 | |
Dibromobipheny1 | n.d. | 5 | |
Tribromobipheny1 | n.d. | 5 | |
Tetrabromobipheny1 | n.d. | 5 | |
Pentabromobipheny1 | n.d. | 5 | |
Hexabromobipheny1 | n.d. | 5 | |
Heptabromobipheny1 | n.d. | 5 | |
Octabromobipheny1 | n.d. | 5 | |
Nonabromobipheny1 | n.d. | 5 | |
Decabromobipheny1 | n.d. | 5 | |
Sum of PBDEs | n.d. | - | |
Monobromodipheny1 ether | n.d. | 5 | |
Dibromodipheny1 ether | n.d. | 5 | |
Tribromodipheny1 ether | n.d. | 5 | |
Tetrabromodipheny1 ether | n.d. | 5 | |
Pentabromodipheny1 ether | n.d. | 5 | |
Hexabromodipheny1 ether | n.d. | 5 | |
Heptabromodipheny1 ether | n.d. | 5 | |
Octabromodipheny1 ether | n.d. | 5 | |
Nonabromodipheny1 ether | n.d. | 5 | |
Decabromodipheny1 ether | n.d. | 5 |