F1 Sealant
Test Items |
Result |
Inspection method |
Adhesion Strength (Base: Cement Mortar) w/o Primer |
18.5 kgf/cm2 |
CNS 8083 |
Adhesion Strength (Base: Steel Board) w/o Primer |
30.2 kgf/cm2 |
CNS 10757 |
Water Permeability |
0.1 ml |
CNS 4684 |
Tensile Strength |
64 kgf/cm2 |
CNS 6483 |
Elongation Rate |
390% |
CNS 6483 |
Tear Resistance |
28 kgf/cm2 |
CNS 6483 |
Coefficient of Elasticity |
7% |
CNS 6483 |
Wear Resistance (CNS 6483) Abrasion Loss |
0.14 g |
CNS 6483 |
Solar Direct Reflectance (Test side: Gloss side)(340~2800nm) |
84.0% |
CNS 12381 |
Water Resistance (23℃,30 days) |
Normal |
CNS 10757 |
SGS Test Report (Test Results) (Unit):mg / kg
ROHS ( Test ltems ) |
Method(Refer to) |
(Result)( No.1 ) |
( MDL ) |
Cadmium(Cd) |
(1) |
n.d. |
2 |
Lead( Pb ) |
(2) |
n.d. |
2 |
Mercury(Hg) |
(3) |
n.d. |
2 |
Hexavalent Chromium Cr(VI)by alkaline extraction |
(4) |
n.d. |
2 |
Sum of PBBs |
(5) |
n.d. |
- |
Monobromobipheny1 |
n.d. |
5 |
Dibromobipheny1 |
n.d. |
5 |
Tribromobipheny1 |
n.d. |
5 |
Tetrabromobipheny1 |
n.d. |
5 |
Pentabromobipheny1 |
n.d. |
5 |
Hexabromobipheny1 |
n.d. |
5 |
Heptabromobipheny1 |
n.d. |
5 |
Octabromobipheny1 |
n.d. |
5 |
Nonabromobipheny1 |
n.d. |
5 |
Decabromobipheny1 |
n.d. |
5 |
Sum of PBDEs |
n.d. |
- |
Monobromodipheny1 ether |
n.d. |
5 |
Dibromodipheny1 ether |
n.d. |
5 |
Tribromodipheny1 ether |
n.d. |
5 |
Tetrabromodipheny1 ether |
n.d. |
5 |
Pentabromodipheny1 ether |
n.d. |
5 |
Hexabromodipheny1 ether |
n.d. |
5 |
Heptabromodipheny1 ether |
n.d. |
5 |
Octabromodipheny1 ether |
n.d. |
5 |
Nonabromodipheny1 ether |
n.d. |
5 |
Decabromodipheny1 ether |
n.d. |
5 |
Note : 1. mg / kg = ppm ; 0.1wt %=1000 ppm 2.n.d.=Not Detected 3..MDL = Method Detection Limit 4."_" =Not Regulated